The following datasheet provides further information about UNS C72200 chromium-bearing copper nickel alloy.
Chemical Composition
The following table shows the chemical composition of UNS C72200 chromium-bearing copper nickel alloy.
| Element | Content (%) |
|---|---|
| Cu | 82.0 |
| Ni | 16.0 |
| Cr | 0.5 |
| Fe | 0.8 |
| Mn | 0.5 |
Physical Properties
The physical properties of UNS C72200 chromium-bearing copper nickel alloy are outlined in the following table.
| Properties | Metric | Imperial |
|---|---|---|
| Density | 8.94 g/cm3 | 0.323 lb/in³ |
Mechanical Properties
The mechanical properties of UNS C72200 chromium-bearing copper nickel alloy are tabulated below.
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength (O61 temper) | 315 MPa | 45700 psi |
| Tensile strength (H04 temper) | 480 MPa | 69600 psi |
| Yield strength (@strain 0.200 %, O61 temper) | 125 MPa | 18100 psi |
| Yield strength (@strain 0.200 %, H04 temper) | 455 MPa | 66000 psi |
| Elongation at break (H04 temper) | 6.00% | 6.00% |
| Elongation at break (O61 temper) | 46.00% | 46.00% |
| Elastic modulus | 117 GPa | 17000 ksi |
| Poisson’s ratio | 0.34 | 0.34 |
| Shear modulus | 55.0 GPa | 7980 ksi |