1.7380 10CrMo910 10CrMo9-10 12CrMo9-10 1.7375 Forged Forging steel Rings Rolled Rings Forging Sleeves Bushes Bushing Pipes Piping tubes tubings barrels Casing Cases Shells cylinders hubs housings Part
型号:
parameters1:
parameters2:
parameters3:
We are professional 1.7380 10CrMo910 10CrMo9-10 12CrMo9-10 1.7375 Forged Forging steel Rings Rolled Rings Forging Sleeves Bushes Bushing Pipes Piping tubes tubings barrels Casing Cases Shells cylinders hubs housings Parts Pieces Material Products from china
Chemical composition % of steel 12CrMo9-10 (1.7375): EN 10028-2-2003C | Si | Mn | Ni | P | S | Cr | Mo | N | Al | Cu |
0.1 - 0.15 | max 0.3 | 0.3 - 0.8 | max 0.3 | max 0.015 | max 0.01 | 2 - 2.5 | 0.9 - 1.1 | max 0.012 | 0.01 - 0.04 | max 0.25 |
Mechanical properties of steel 12CrMo9-10 (1.7375)
Nominal thickness (mm): | to 250 |
|
Rm - Tensile strength (MPa) (+NT) | 540-690 |
Nominal thickness (mm): | to 250 |
|
ReH - Minimum yield strength (MPa) (+NT) | 355 |
|
KV - Impact energy (J) transverse, (+NT) | -20° 27 | 0° 40 | +20° 70 |
Nominal thickness (mm): | to 250 |
|
A - Min. elongation at fracture (%) (+NT) | 18
|
Chemical composition % of steel 10CrMo9-10 (1.7380): EN 10028-2-2003According EN 10216-2 chemical composition: 0.3 < Mn < 0.7; |
C | Si | Mn | P | S | Cr | Mo | N | Cu |
0.08 - 0.14 | max 0.5 | 0.4 - 0.8 | max 0.02 | max 0.01 | 2 - 2.5 | 0.9 - 1.1 | max 0.012 | max 0.3 |
Mechanical properties of steel 10CrMo9-10 (1.7380)
Nominal thickness (mm): | to 60 | 60 - 100 | 100 - 150 | 150 - 250 |
|
Rm - Tensile strength (MPa) | 480-630 | 470-620 | 460-610 | 450-600 |
Nominal thickness (mm): | to 16 | 16 - 40 | 40 - 60 | 60 - 100 | 100 - 150 | 150 - 250 |
|
ReH - Minimum yield strength (MPa) | 310 | 300 | 290 | 280 | 260 | 250 |
Nominal thickness(mm): | to 16 | 16 - 40 | 40 - 60 |
|
Rp0.2 0.2% proof strength (MPa) (+NT) | 280 | 280 | 270 |
|
KV - Impact energy (J) transverse, | +20° 27-31 |
|
KV - Impact energy (J) longitud., | +20° 40 |
|
A - Min. elongation at fracture (%) longitud., (+NT) | 22 |
|
A - Min. elongation at fracture (%) transverse, (+NT) | 20 |