Chemical composition % of steel 16Mo3 (1.5415): EN 10028-2-2003| C | Si | Mn | Ni | P | S | Cr | Mo | N | Cu |
| 0.12 - 0.2 | max 0.35 | 0.4 - 0.9 | max 0.3 | max 0.025 | max 0.01 | max 0.3 | 0.25 - 0.35 | max 0.012 | max 0.3 |
Mechanical properties of steel 16Mo3 (1.5415)
| Nominal thickness (mm): | to 60 | 60 - 100 | 100 - 150 | 150 - 250 |
|
| Rm - Tensile strength (MPa) (+N) | 440-590 | 430-580 | 420-570 | 410-570 |
| Nominal thickness (mm): | to 250 | 250 - 500 |
|
| Rm - Tensile strength (MPa) (+QT) | 440-570 | 420-550 |
| Nominal thickness (mm): | to 16 | 16 - 40 | 40 - 60 | 60 - 100 | 100 - 150 | 150 - 250 |
|
| ReH - Minimum yield strength (MPa) (+N) | 275 | 270 | 260 | 240 | 220 | 210 |
| Nominal thickness (mm): | to 250 | 250 - 500 |
|
| ReH - Minimum yield strength (MPa) (+QT) | 265 | 250 |
|
| KV - Impact energy (J) transverse, (+N) | +20°
27 |
|
| KV - Impact energy (J) longitud., (+QT) | +20°
50 |
|
| KV - Impact energy (J) transverse, (+QT) | +20°
34 |
|
| KV - Impact energy (J) longitud., | +20°
40 |
|
| A - Min. elongation at fracture (%) longitud., (+QT) | 23 |
|
| A - Min. elongation at fracture (%) transverse, (+N) | 20 |
| Nominal thickness (mm): | to 40 | 40 - 60 | 60 - 100 | 100 - 150 |
|
| A - Min. elongation at fracture (%) (+N) | 24 | 23 | 22 | 19 |