A multiple tube bundle heat exchanger includes axially opposite tube plates, a housing, and a plurality of tube bundles disposed between the tube plates. Each of the tube bundles is an independent tube bundle subassembly forming an integral unit having at least one heat exchanger tube with two axial tube ends.
Chemical composition % of steel X2CrNiN23-4 (1.4362): EN 10088-2-2005Elements not listed in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast.
|
C | Si | Mn | Ni | P | S | Cr | Mo | N | Cu |
max 0.03 | max 1 | max 2 | 3.5 - 5.5 | max 0.035 | max 0.015 | 22 - 24 | 0.1 - 0.6 | 0.05 - 0.2 | 0.1 - 0.6 |
Mechanical properties of steel X2CrNiN23-4 (1.4362)
|
Rm - Tensile strength (MPa) (+A) | 600-850 |
|
Rm - Tensile strength (MPa) (+AT) | 600-820 |
|
Rp0.2 0.2% proof strength (MPa) (+A) | 400-450 |
|
Rp0.2 0.2% proof strength (MPa) (+AT) | 400 |
|
KV - Impact energy (J) transverse, (+A) | +20° 90 | -40° 40 |
|
KV - Impact energy (J) longitud., (+A) | +20° 100-120 |
|
KV - Impact energy (J) longitud., (+AT) | 20° 120 |
|
A - Min. elongation at fracture (%) (+A) | 20-25 |
|
A - Min. elongation at fracture (%) longitud., (+AT) | 25 |
|
A - Min. elongation at fracture (%) transverse, (+AT) | 25 |
Brinell hardness (HB): (+A) | 260 |
Brinell hardness (HB): (+AT) | 290
|