1.4034 X46Cr13 Forged Forging steel Rings Rolled Rings Forging Sleeves Bushes Bushing Pipes Piping tubes tubings barrels Casing Cases Shells cylinders hubs housings Parts Pieces Material Products
型号：
parameters1：
parameters2：
parameters3：
We are professional 1.4034 X46Cr13 Forged Forging steel Rings Rolled Rings Forging Sleeves Bushes Bushing Pipes Piping tubes tubings barrels Casing Cases Shells cylinders hubs housings Parts Pieces Material Products from china
Chemical composition % of steel X46Cr13 (1.4034): EN 10088-2-2005Tighter carbon ranges may be agreed at the time of enquery and order
Particular ranges of sulphur content may provide improvement of particular properties. For machinability a controlled sulphur content of 0.015 % to 0.030% is recommended and permitted. For weldability, a controlled sulphur content of 0.008 % to 0.030 % is recommended and permitted. For polishability, a controlled sulphur content of 0.015 % max is recommended.
Elements not listed in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast.
|
| C | Si | Mn | P | S | Cr |
| 0.43 - 0.5 | max 1 | max 1 | max 0.04 | max 0.015 | 12.5 - 14.5 |
Mechanical properties of steel X46Cr13 (1.4034)
|
| Rm - Tensile strength (MPa) (+A) | 780 |
|
| Rm - Tensile strength (MPa) (+QT800) | 850-1000 |
|
| Rp0.2 0.2% proof strength (MPa) +QT800 | 650 |
|
| KV - Impact energy (J) longitud., | +20°
12 |
|
| A - Min. elongation at fracture (%) | 10-12 |
| Brinell hardness (HB): (+A) | 245 |