1.4034 X46Cr13 Forging Forged Feed Mill Pellet Ring Dies Pellet Mill Ring Dies Animal Feed Pellet Mill Ring Die Pellet Machine Ring die Pellet Press Ring Die Wood Pellet Machine Ring Die
型号：
parameters1：
parameters2：
parameters3：
parameters1：
parameters2：
parameters3：
We are professional 1.4034 X46Cr13 Forging Forged Feed Mill Pellet Ring Dies Pellet Mill Ring Dies Animal Feed Pellet Mill Ring Die Pellet Machine Ring die Pellet Press Ring Die Wood Pellet Machine Ring Die Factory from china
Chemical composition % of steel X46Cr13 (1.4034): EN 10088-2-2005
Mechanical properties of steel X46Cr13 (1.4034)
Ring die is a main part of pellet mill to produce animal feed, wood pellets, and other granules.we usually manufacture the products as per customers drawing.
The Material of ring dies is mainly X46Cr13 (stainless steel)and 20MnCr5 (alloy steel)
Hardness of ring dies that we could reach is : HRC54-60.
Following is our production capabilities of ring dies
Ring die： Straight type/Stepped type
Outer diameter up to 1500mm
Taper type up to 20mm diameter
Diameter of ring die channel holes - from 1,8mm up to 14mm
Channel length from 55mm up to 104mm
Flat die： Straight type/Stepped type
Outer diameter up to 1500mm
Taper type up to 16mm diameter
Pellet ring dies must resist abrasion, corrosion from chemical exposure and breakage caused by the physical stresses of pellet formation. The optimum die combines high resistance to abrasion, breakage and corrosion with maximum productivity. Our expertise enables us to precisely match the die specification to your required formulation, even if it means customizing a die pattern to meet your exact needs.
Please send us the drawing and quantity of ring dies that you need, we are glad to quote the best price for your side
| Tighter carbon ranges may be agreed at the time of enquery and order Particular ranges of sulphur content may provide improvement of particular properties. For machinability a controlled sulphur content of 0.015 % to 0.030% is recommended and permitted. For weldability, a controlled sulphur content of 0.008 % to 0.030 % is recommended and permitted. For polishability, a controlled sulphur content of 0.015 % max is recommended. Elements not listed in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast. |
| C | Si | Mn | P | S | Cr |
| 0.43 - 0.5 | max 1 | max 1 | max 0.04 | max 0.015 | 12.5 - 14.5 |
Mechanical properties of steel X46Cr13 (1.4034)
| Rm - Tensile strength (MPa) (+A) | 780 |
| Rm - Tensile strength (MPa) (+QT800) | 850-1000 |
| Rp0.2 0.2% proof strength (MPa) +QT800 | 650 |
| KV - Impact energy (J) longitud., | +20° 12 |
| A - Min. elongation at fracture (%) | 10-12 |
| Brinell hardness (HB): (+A) | 245 |