SAF 2304 UNS S32304 1.4362 X2CrNiN23-4 Alloy 2304 Forged Forging steel Rings Rolled Rings Forging Sleeves Flanges Bushes Bushing Pipes Piping tubes tubings barrels Casing Cases Shells cylinders hubs h
型号：
parameters1：
parameters2：
parameters3：
We are professional SAF 2304 UNS S32304 1.4362 X2CrNiN23-4 Alloy 2304 Forged Forging steel Rings Rolled Rings Forging Sleeves Flanges Bushes Bushing Pipes Piping tubes tubings barrels Casing Cases Shells cylinders hubs housings Parts Pieces Material Products from china
Elements not listed in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast.
|
| C | Si | Mn | Ni | P | S | Cr | Mo | N | Cu |
| max 0.03 | max 1 | max 2 | 3.5 - 5.5 | max 0.035 | max 0.015 | 22 - 24 | 0.1 - 0.6 | 0.05 - 0.2 | 0.1 - 0.6 |
Mechanical properties of steel X2CrNiN23-4 (1.4362)
|
| Rm - Tensile strength (MPa) (+A) | 600-850 |
|
| Rm - Tensile strength (MPa) (+AT) | 600-820 |
|
| Rp0.2 0.2% proof strength (MPa) (+A) | 400-450 |
|
| Rp0.2 0.2% proof strength (MPa) (+AT) | 400 |
|
| KV - Impact energy (J) transverse, (+A) | +20°
90 | -40°
40 |
|
| KV - Impact energy (J) longitud., (+A) | +20°
100-120 |
|
| KV - Impact energy (J) longitud., (+AT) | 20°
120 |
|
| A - Min. elongation at fracture (%) (+A) | 20-25 |
|
| A - Min. elongation at fracture (%) longitud., (+AT) | 25 |
|
| A - Min. elongation at fracture (%) transverse, (+AT) | 25 |
| Brinell hardness (HB): (+A) | 260 |
| Brinell hardness (HB): (+AT) | 290 |