A182-F55 UNS S32760 ZERON 100 1.4501 X2CrNiMoWCuWN 25-7-4 Forged Forging Rings Rolled Rings Forging Sleeves Flanges Bushes Bushing Pipes Piping tubes tubings barrels Casing Cases Shells cylinders hub
型号：
parameters1：
parameters2：
parameters3：
We are professional A182-F55 UNS S32760 ZERON 100 1.4501 X2CrNiMoWCuWN 25-7-4 Forged Forging Rings Rolled Rings Forging Sleeves Flanges Bushes Bushing Pipes Piping tubes tubings barrels Casing Cases Shells cylinders hubs housings Parts Pieces Material Products from china
Chemical composition % of steel X2CrNiMoCuWN25-7-4 (1.4501): EN 10088-2-2005Elements not listed in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast.
|
| C | Si | Mn | Ni | P | S | Cr | Mo | W | N | Cu |
| max 0.03 | max 1 | max 1 | 6 - 8 | max 0.035 | max 0.015 | 24 - 26 | 3 - 4 | 0.5 - 1 | 0.2 - 0.3 | 0.5 - 1 |
Mechanical properties of steel X2CrNiMoCuWN25-7-4 (1.4501)
|
| Rm - Tensile strength (MPa) (+A) | 730-930 |
|
| Rm - Tensile strength (MPa) (+AT) | 800-1000 |
|
| Rp0.2 0.2% proof strength (MPa) (+A) | 530 |
|
| Rp0.2 0.2% proof strength (MPa) (+AT) | 550 |
|
| KV - Impact energy (J) transverse, (+A) | +20°
90 | -40°
40 |
|
| KV - Impact energy (J) transverse, (+AT) | +20°
100 | -40°
40 |
|
| KV - Impact energy (J) longitud., (+AT) | +20°
100 |
|
| A - Min. elongation at fracture (%) (+A) | 25 |
|
| A - Min. elongation at fracture (%) longitud., (+AT) | 20 |
| Brinell hardness (HB): (+A) | 290 |
| Brinell hardness (HB): (+AT) | 310
|