Incoloy 926 UNS N08926 1.4529 Alloy 926 X1NiCrMoCuN25-20-7 Forged Forging Rings Rolled Rings Forging Sleeves Flanges Bushes Bushing Pipes Piping tubes tubings barrels Casing Cases Shells cylinders hub
型号：
parameters1：
parameters2：
parameters3：
We are professional Incoloy 926 UNS N08926 1.4529 Alloy 926 X1NiCrMoCuN25-20-7 Forged Forging Rings Rolled Rings Forging Sleeves Flanges Bushes Bushing Pipes Piping tubes tubings barrels Casing Cases Shells cylinders hubs housings Parts Pieces Material Products from china
Chemical composition % of steel X1NiCrMoCuN25-20-7 (1.4529): EN 10088-2-2005Elements not listed in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast.
|
| C | Si | Mn | Ni | P | S | Cr | Mo | N | Cu |
| max 0.02 | max 0.5 | max 1 | 24 - 26 | max 0.03 | max 0.01 | 19 - 21 | 6 - 7 | 0.15 - 0.25 | 0.5 - 1.5 |
Mechanical properties of steel X1NiCrMoCuN25-20-7 (1.4529)
|
| Rm - Tensile strength (MPa) (+A) | 650-850 |
|
| Rm - Tensile strength (MPa) (+AT) | 600-800 |
|
| Rp0.2 0.2% proof strength (MPa) (+A) | 300-340 |
|
| Rp0.2 0.2% proof strength (MPa) (+AT) | 270-300 |
|
| KV - Impact energy (J) transverse, (+A) | +20°
60 | -196°
60 |
|
| KV - Impact energy (J) longitud., (+A) | +20°
100 |
|
| KV - Impact energy (J) longitud., (+AT) | +20°
100-120 |
|
| KV - Impact energy (J) transverse, (+AT) | +20°
60-90 | -196°
60 |
|
| A - Min. elongation at fracture (%) (+A) | 35-40 |
|
| A - Min. elongation at fracture (%) longitud., (+AT) | 35 |
|
| A - Min. elongation at fracture (%) transverse, (+AT) | 30 |
| Brinell hardness (HB): (+A) | 250 |
| Brinell hardness (HB): (+AT) | 220 |