Incoloy 926 UNS N08926 1.4529 Alloy 926 X1NiCrMoCuN25-20-7 Forged Forging Round Bars Hollow Bars Shafts Square rectangular rectangle Blocks Discs Disks Plates Flat Bar
型号:
parameters1:
parameters2:
parameters3:
We are professional Incoloy 926 UNS N08926 1.4529 Alloy 926 X1NiCrMoCuN25-20-7 Forged Forging Round Bars Hollow Bars Shafts Square rectangular rectangle Blocks Discs Disks Plates Flat Bars from china
Chemical composition % of steel X1NiCrMoCuN25-20-7 (1.4529): EN 10088-2-2005Elements not listed in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast.
|
C | Si | Mn | Ni | P | S | Cr | Mo | N | Cu |
max 0.02 | max 0.5 | max 1 | 24 - 26 | max 0.03 | max 0.01 | 19 - 21 | 6 - 7 | 0.15 - 0.25 | 0.5 - 1.5 |
Mechanical properties of steel X1NiCrMoCuN25-20-7 (1.4529)
|
Rm - Tensile strength (MPa) (+A) | 650-850 |
|
Rm - Tensile strength (MPa) (+AT) | 600-800 |
|
Rp0.2 0.2% proof strength (MPa) (+A) | 300-340 |
|
Rp0.2 0.2% proof strength (MPa) (+AT) | 270-300 |
|
KV - Impact energy (J) transverse, (+A) | +20° 60 | -196° 60 |
|
KV - Impact energy (J) longitud., (+A) | +20° 100 |
|
KV - Impact energy (J) longitud., (+AT) | +20° 100-120 |
|
KV - Impact energy (J) transverse, (+AT) | +20° 60-90 | -196° 60 |
|
A - Min. elongation at fracture (%) (+A) | 35-40 |
|
A - Min. elongation at fracture (%) longitud., (+AT) | 35 |
|
A - Min. elongation at fracture (%) transverse, (+AT) | 30 |
Brinell hardness (HB): (+A) | 250 |
Brinell hardness (HB): (+AT) | 220 |