Alloy Composition of AISI 316N 316 N SS 316N TP316N SUS 316N 
 
Iron (Fe)61.9 to 71.9 %
Chromium (Cr)16 to 18 %
Nickel (Ni)10 to 14 %
Molybdenum (Mo)2.0 to 3.0 %
Manganese (Mn)0 to 2.0 %
Silicon (Si)0 to 0.75 %
Nitrogen (N)0.1 to 0.16 %
Carbon (C)0 to 0.080 %
Phosphorus (P)0 to 0.045 %
Sulfur (S)
 
Material Properties of AISI 316N 316 N SS 316N TP316N SUS 316N 
 
Base Metal Price31 % rel
Density7.9 g/cm3 (490 lb/ft3)
Elastic (Young's, Tensile) Modulus200 GPa (29 x 106 psi)
Electrical Conductivity2.3 % IACS
Electrical Resistivity Order of Magnitude-6 10x Ω-m
Elongation at Break9.2 to 40 %
Modulus of Resilience (Unit Resilience)200 to 1890 kJ/m3
Poisson's Ratio0.28
PREN (Pitting Resistance)20
Specific Heat Capacity500 J/kg-K
Strength to Weight Ratio80 to 150 kN-m/kg
Tensile Strength: Ultimate (UTS)630 to 1190 MPa (91 to 170 x 103 psi)
Tensile Strength: Yield (Proof)280 to 870 MPa (41 to 130 x 103 psi)
Thermal Conductivity15 W/m-K
Thermal Diffusivity3.8 m2/s
Thermal Expansion13 µm/m-K
Unit Rupture Work (Ultimate Resilience)